We transformed a data envelopment analysis (DEA) optimization model into a robust second-order cone equivalent to immunize against output perturbation in an uncertainty set. The robust DEA framework was then used to assess the effect of a wood hardening treatment using methyl methacrylate (MMA) on selected hybrid poplar clones. Because the performance of MMA-hardened hybrid poplar clones varies across clones, ranking hardened clones is crucial for developing hardening treatments for specific industrial applications. The numerical results demonstrate that the hardening treatment can be optimized by applying the proposed DEA framework to select the best hybrid poplar clone types and the optimal amount of impregnated chemicals.

Wood of fast-growing hybrid poplars, consisting of six 6-year-old clones in one plantation in Quebec, was impregnated with methyl methacrylate (MMA) and then polymerized by heat/catalyst method. The mechanical properties (static bending and compressive strength) of poplar clones and its MMA-hardened wood were investigated. Significant differences were observed among clones in bending and compression strength parallel to grain. Hardening treatment has also considerably improved all strength properties except for strain at rupture in static bending. The effects of density on mechanical properties were inconsistent, especially for hardened wood. Density was not the most important factor affecting strength properties. The improved properties of MMA-hardened hybrid poplar were comparable to some commercial hardwood species.

In an effort to achieve high mechanical performance and improved dimensional stability, densification combined with oil-heat treatment (OHT) was performed. In our previous study, OHT was successfully applied to densified veneer, which resulted in improved dimensional stability. In the present study, the impact of OHT on densified wood veneer hygroscopicity and mechanical properties was determined. OHT at 180, 200, and 220ºC for 1, 2, and 3 hours was applied to densified Aspen (Populus tremuloides) veneers. OHT was found to be an efficient treatment to reduce the hygroscopicity of densified aspen veneers, although OHT had a negative impact on Brinell hardness. However, due to the contribution of densification, the hardness of oil-heat treated veneers was still two to three times higher than that of non-densified veneers. Similar results were found for tensile strength. Bending strength increased slightly at low OHT temperature, and then decreased at high temperature. Bending strength of oil-heat treated densified veneer samples was higher than that of non-densified ones. No significant effect of OHT was found on tensile MOE, but bending MOE increased after OHT. Compared to OHT duration, OHT temperature had a larger impact on densified wood hygroscopicity and mechanical properties.

Wood–plastic composites (WPC) were produced with white birch pulp fibers of different aspect ratios (length-to-diameter), high-density polyethylene, and using two common processes: extrusion or injection molding. Three additive levels were also used: no additive, compatibility agent, and process lubricant. Fiber size was measured with an optical fiber quality analyzer. Tensile properties of WPC were measured and modeled as a function of fiber aspect ratio. Models were fitted to experimental values using the minimum sum of squared error method. A shift from the oriented fiber case (injection molding) to the randomly oriented fiber case (extrusion) was achieved using a fiber orientation factor. Fiber/matrix stress transfer increased with increasing fiber aspect ratio. Stress transfer was reduced with the use of process lubricant. Unexpectedly, the compatibility agent had the same effect. Fiber strength and stiffness contributions to the composite were lower than those of intrinsic fiber properties.